Macro-residual strains produced by load cycles on elastic-brittle composites are analytically expressed in terms of the effective thermal expansion coefficients of the composite as affected by the damage states developing during the cycling. Limiting values of residual strain are evaluated for unidirectional fiber composites and cross-ply laminates. Frictional losses due to internal sliding are not considered.
פותח על ידי קלירמאש פתרונות בע"מ -
הספר "אוצר וולקני"
אודות
תנאי שימוש
Macro-residual strains due to cyclic loading of composites
6
Hashin, Z., Faculty of Engineering, Tel Aviv University, Tel Aviv, Israel, Faculty of Engineering, Tel-Aviv University, Ramat-Aviv, Israel
Rosen, B.W., Materials Sciences Corp., Fort Washington, PA, United States
Macro-residual strains due to cyclic loading of composites
Macro-residual strains produced by load cycles on elastic-brittle composites are analytically expressed in terms of the effective thermal expansion coefficients of the composite as affected by the damage states developing during the cycling. Limiting values of residual strain are evaluated for unidirectional fiber composites and cross-ply laminates. Frictional losses due to internal sliding are not considered.